Haynes 188 is a cobalt-nickel-chromium-tungsten alloy that combines excellent high-temperature strength with outstanding resistance to oxidizing environments up to 2000°F (1095°C) for prolonged periods. The controlled addition of lanthanum gives it superior oxidation resistance compared to Haynes 25.
- الأشكال الشائعة: Sheet, Strip, Plate, Bar.
- الميزة الرئيسية: Outstanding oxidation resistance + Thermal stability.
- Addition: Lanthanum modified for tenacious oxide scale.
- قابلية التصنيع: Excellent ductility and weldability.
Haynes 188 is the material of choice for critical components in gas turbine engines, such as combustors and flame holders. While sharing the strength of Haynes 25, the addition of Lanthanum allows 188 to form a protective oxide scale that adheres tightly even during severe thermal cycling, preventing the material from degrading over time.
Superior Oxidation Resistance
Resists oxidation at temperatures up to 2100°F (1150°C). The minute Lanthanum addition creates an incredibly stable and adherent oxide layer.
الاستقرار الحراري
Maintains ductility after long-term aging at elevated temperatures better than Haynes 25, reducing the risk of embrittlement.
Hot Corrosion Resistance
Excellent resistance to sulfate deposit hot corrosion, making it ideal for jet engines operating in marine environments.
| العنصر | المحتوى (%) |
|---|---|
| الكوبالت (Co) | 39.0 min (Balance) |
| النيكل (ني) | 20.0 - 24.0 |
| الكروم (Cr) | 21.0 - 23.0 |
| التنجستن (W) | 13.0 - 15.0 |
| الحديد (Fe) | 3.0 كحد أقصى |
| Lanthanum (La) | 0.03 - 0.15 |
| الكربون (C) | 0.05 - 0.15 |
*Note: The Lanthanum addition is the key differentiator for oxidation performance.
| نموذج المنتج | المعايير (AMS) |
|---|---|
| ورقة، شريط، لوحة، صفيحة | AMS 5608 |
| القضبان والمطروقات والخواتم | AMS 5772 |
| Pipe & Tube | AMS 5586 |
| الممتلكات | القيم النموذجية (درجة حرارة الغرفة) |
|---|---|
| قوة الشد | 135 - 150 ksi (930 - 1035 MPa) |
| قوة الخضوع (إزاحة 0.2%) | 60 - 75 ksi (415 - 515 MPa) |
| الاستطالة | 45 - 55 % |
| الصلابة (روكويل ب) | 90 - 98 HRB |
Combustor Liners
The primary application: inner walls of jet engine combustors exposed to extreme heat and gas velocity.
Flame Holders
Components in afterburners and exhaust ducts that stabilize the flame.
Transition Ducts
Ducting that guides hot gases from the combustor to the turbine section.
Spray Bars
Fuel injection systems located within the hot section of the engine.