Maraging 350
Maraging 350 offers the highest strength of the 18% nickel maraging steel family. It is an ultra-high-strength steel that contains Cobalt and Molybdenum, and higher Titanium content than the 300 grade. It provides a nominal yield strength of 350,000 psi (2415 MPa).
- Forme comuni: Round Bar, Forged Billet.
- Caratteristiche principali: Extreme Yield Strength (350 ksi).
- Hardness: Up to 57-60 HRC after aging.
- Compromise: Lower toughness than 250 or 300 grades.
Select Maraging 350 when your design demands the absolute maximum tensile and yield strength available in a maraging alloy. While it sacrifices some fracture toughness compared to the 300 grade, its ability to withstand massive centrifugal forces and compressive loads makes it indispensable for specialized high-performance equipment.
Forza estrema
Achieves yield strengths of 350,000 psi, making it one of the strongest structural metals available.
High Hardness
Can be age-hardened to approximately 57-60 Rockwell C, providing excellent resistance to surface wear and deformation.
Heat Resistance
Maintains substantial strength up to 800°F (427°C), allowing it to perform in high-stress, high-temperature environments.
| Elemento | Contenuto (%) |
|---|---|
| Nichel (Ni) | 18.0 - 19.0 |
| Cobalto (Co) | 11.5 - 12.5 |
| Molibdeno (Mo) | 4.6 - 5.2 |
| Titanio (Ti) | 1.3 - 1.6 |
| Alluminio (Al) | 0.05 - 0.15 |
| Ferro (Fe) | Equilibrio |
*Note: The significantly higher Titanium and Cobalt levels drive the strength increase over Grade 300.
| Forma del prodotto | Standards (AMS / ASTM / MIL) |
|---|---|
| Bar, Forgiati | AMS 6515 |
| Military Spec | MIL-S-46850 Type IV |
| Chemical Comp | ASTM A538 (Grade C) |
| Proprietà | Valori tipici (temperatura ambiente) |
|---|---|
| Resistenza allo snervamento (offset 0,2%) | 340 - 360 ksi (2344 - 2482 MPa) |
| Ultimate Tensile Strength | 350 - 370 ksi (2415 - 2550 MPa) |
| Allungamento | 6 - 8 % |
| Reduction of Area | 30 - 40 % |
| Durezza (Rockwell C) | 57 - 60 HRC |
| Fracture Toughness (KIC) | ~40 ksi√in |
*Note: Properties achieved after aging at 900-925°F for 6-12 hours.
Gas Centrifuges
Ultra-high-speed rotors for isotope separation requiring extreme tensile strength and balance.
Rocketry
Solid propellant motor cases and structural components where weight savings are critical.
Tooling & Dies
Core pins and extrusion dies for aluminum and zinc casting that require high hot hardness.
Flywheels
Kinetic energy storage systems operating at extreme RPMs.